would render even a faint tint conspicuous. The substances employed are the same as those used for the manufacture of sheet-glass, viz pure sand, a pure form of carbonate of lime and sulphate of soda, with the addition of a suitable proportion of carbon in the form of coke, charcoal or anthracite coal.
The glass to be used for the production of plate is universally melted. in. pots or crucibles and not in open tank furnaces. When the glass is completely melted and "fine", i.e. free from bubbles, it is allowed to cool down to a certain extent so as to become viscous or pasty. The whole pot, with its content of viscous glass, is then removed bodily from the furnace by means of huge tongs and is transported to a crane, which grips the pot, raises it, and ultimately tips it over so as to pour the glass upon the slab of the rolling-table. In most modern work the greater part of these operations, as well as the actual rolling of the glass, is carried out by mechanical means, steam power and subsequently electrical power having been successfully applied to this purpose; the handling of the great weights of glass required for the largest sheets of plate-glass which are produced at the present time would, indeed, be impossible without the aid of machinery. The casting-table usually consists of a perfectly smooth cast-iron slab; frequently built up of a number of pieces carefully fitted together; mounted upon a low, massive truck running upon rails so that it can be readily moved to any desired position in the casting-room. The viscous mass having been thrown on the casting-table, a large and heavy roller passes over it and spreads it out into a sheet. Rollers up to 5 tons in weight are employed and are now generally driven by power. The width of the sheet or plate is regulated by moving guides which are placed in front of the roller and are pushed along by it, while its thickness is regulated by raising or lowering the roller relatively to the surface of the table. Since the surfaces produced by rolling have to be ground and polished, it is essential that the glass should leave the rolling-table with a smooth a surface a possible, so that great care is required in this part of the process. It is, however, equally important that the glass as a whole should be flat and remains flat during the process of gradual cooling (annealing) otherwise great thicknesses of glass would have be ground away at the projecting parts of the sheet. The annealing process is therefore carried out in a manner differing essentially from that in used for any other variety of flat glass and nearly resembling that used for optical glass. The rolled sheet is left on the casting-table until it has set sufficiently to be pushed over a flat iron plate without risk of distortion Meanwhile the table has been placed in front of the opening of one of the large annealing kilns and the slab of glass is carefully pushed into the kiln. The annealing kilns are large fire-brick chambers of small height but with sufficient floor area to accommodate four or six large slabs, and the slabs are placed directly upon the floor of the kiln, which is built up of carefully dressed blocks of burnt fire-clay resting upon a bed of sand; in order to avoid any risk of working or buckling in this floor these blocks are set slightly apart and thus have room to expand freely when heated. Before the glass is introduced, the annealing kiln is heated to dull red by means of coal fires in grates which are provided at the ends or sides of the kiln for that purpose. When the floor of the. kiln has been covered with slabs of glass the opening is carefully built up and luted with fire-bricks. and fire-clay, and the whole is then allowed to cool. In the walls and floor of the kiln special cooling channels or air passages are provided and by gradually opening these to atmospheric circulation the cooling is considerably accelerated while a very even distribution of temperature is obtained; by these means even the largest slabs can now be cooled in three or four days and, are nevertheless sufficiently well annealed to be free from any serious internal stress. From the annealing kiln the slabs of glass are transported the cutting room, where they are cut. square, defective slabs being rejected or cut down to smaller sizes. The glass at this stage has a comparatively dull surface and this must now be replaced by that brilliant and perfectly polished surface which is the chief beauty of this variety of glass. The first step in this process is that of grinding the surface down until all projections are removed and a close approximation to a perfect plate is obtained. This operation, like all the subsequent steps in the polishing of the glass, is carried out by powerful machinery. By means of a rotating table either two surfaces of glass, or one surface of glass and one of cast iron, are rubbed together with the interposition of a powerful abrasive such as sand, emery or carborundum. The machinery by which this is done has undergone numerous modifications and improvements, all tending to produce more perfectly plane glass, to reduce the risk of breakage, and to lessen the expenditure of time and power required per sq. yd. of glass to be worked. It is impossible to describe this machinery within the limits of this article but it is notable that the principal difficulties to be overcome arise from the necessity of providing the glass with a perfectly continuous and unyielding support to which it can be firmly attached but from which it can be detached without undue difficulty.
When the surface of the glass has been ground down, to a plane the surface itself is still "grey", i.e. deeply pitted with the marks of the abrasive used in grinding it down; these marks are removed by the process of smoothing; in which the surface is successively ground with abrasives of gradually increasing fineness, leaving ultimately a very smooth and very minutely pitted "grey" surface. This smooth surface is then brilliantly polished by the aid of friction with a rubbing tool covered with a soft substance like leather or felt and fed with a polishing material, such as rouge. A few strokes of such a rubber are sufficient to produce a decidedly polished appearance, but prolonged rubbing under considerable pressure and the use of a polishing paste of a proper consistency are required in order to remove the last trace of pitting from the surface. This entire process must, obviously be applied in turn to each of the two surfaces of the slab of glass. Plate-glass is manufactured in this manner in thicknesses varying from 3/16 in. to 1 in. or even more, while single sheets are produced measuring more than 27 ft. by 13 ft.
"Rolled P1ate" and figured "Rol1ed P1ate" -- Glass for this purpose, with perhaps the exception of the best white and tinted varieties, is now universally produced in tank-furnaces, similar in a general way to those used for sheet-glass except that the furnaces used for "rolled plate" glass of the roughest kinds do not need such minutely careful attention and do not work a so high a temperature. The composition of these glasses is very similar to that of sheet glass, but for the ordinary kinds of rolled plate much less scrupulous selection need be made in the choice of raw materials, especially of the sand.
The glass is taken from the furnace in large iron ladles, which are carried upon slings running on overhead rails; from the ladle the glass is thrown upon the cast-iron bed of a rolling-table; and is rolled into sheet by an iron roller, the process being similar to that employed in making plate glass, but on a smaller scale. The sheet thus rolled is roughly trimmed while hot and soft; so as to remove those portions of glass which have been spoilt by immediate contact with the ladle and the sheet, still soft, is pushed into the open mouth of an annealing tunnel or "lehr", down which it is carried by a system of moving grids.
The surface of the glass produced in this way may be modified by altering the surface of the rolling table; if the table has a smooth surface, the glass will also be more or less smooth, but much dented and buckled on the surface and far from having the smooth face of blown sheet. If the table has a pattern engraved upon it the glass will show the same pattern in relief, the most frequent pattern of the kind being either small parallel ridges or larger ribs crossing to form a lozenge pattern.
The more elaborate patterns found on what is known as "figure rolled plate" are produced in a somewhat different manner; the glass used for this purpose is considerably whiter in colour and much softer than ordinary rolled plate, and instead of being rolled out on a table it is produced by rolling between two moving rollers from which the sheet issues. The pattern is impressed. upon the soft sheet by a printing roller which is brought down upon the glass as it leaves the main rolls. This